T 0212/98 01-12-1999

Reasons for the Decision

1. The appeal complies with the formal requirements of Articles 106 and 108 and Rules 1(1) and 64 EPC. It is therefore admissible.

2. Admissibility of the late filed tests

The opposition division, having considered the results presented in prior art documents as a whole, concluded in point 4.6 of the decision under appeal that sprayed and densified platinum coatings produced by the technique according to D1 should be regarded as being "porous". In response to this finding, the appellants informed the Board in their statement of grounds filed on 2 June 1998 that they had started long term tests, the results of which would be submitted as soon as possible. Enclosed with their letter of 28 September 1999, i.e. two months before the oral proceedings, the test results (document D11) were filed at the EPO and concurrently sent to the respondents. Hence, there was sufficient time for the respondents and for the Board to study and consider the technical content of document D11. The tests, which were not challenged in substance by the respondents, had been performed in an industrial glass production line for four months in order to make sure that any possible interpretation of the vague test conditions according to the patent in suit to assess non-porosity is met. Document D11, thus filling a gap in the appellants' previous reasoning, is highly relevant to the present case to answer the question of whether the disclosure of document D1 - which since the opposition proceedings has been considered as closest prior art - is feasible or not. The respondents' reference to the decision G 10/91 has no bearing on the matter, since document D1 has been already considered in the opposition proceedings. The appellants' tests, demonstrated in document D11, aimed at proving the feasibility of this process which had been denied in the decision under appeal. Consequently, document D11 only adds support to a ground which had already been based on document D1. Therefore, the Board admitted document D11 into the procedure.

3. Article 100(b) EPC; enabling disclosure

In support of their argument that the technical teaching of document D1 is not an enabling disclosure for a skilled person and that the product described in D1 merely represents a "desideratum" within the meaning of decision T 595/90, the respondents, by their letter of 10 October 1997, submitted own test results which showed frothing of the glass on a platinum coating which had not been densified by shot-peening.

In contrast thereto, the appellants, essentially following the teaching given in document D1, have actually produced a platinum coated ceramic substrate exhibiting a surface which is "non-porous" to molten glass within the meaning defined in claim 1 and of the opposed patent as a whole (see document D11). Since the delivery of the screw plunger for a service trial was taken as a basis for an action of infringement against the appellants, the respondents have implicitly conceded that the platinum coated plunger described in D11 in fact has the "non-porous" property required in the patent in suit and, therefore, falls within the scope of claim 1 of the patent at issue. Moreover, the respondents have not doubted the details of the process given in D11 which was used to produce the said platinum coated test plunger. Although this process did not include a densification of the coating by shot-peening, the plunger was satisfactorily operated in contact with molten glass for months, as described by the appellants in document D11. It is true that according to the test process only 50% (instead of 100% as required in D1) of the platinum particles had a size within the range of 20 to 44 µm and that the temperature of 1200 C was below the minimum temperature of 1250 C as required by claim 1 of document D1. These deviations have, however, no negative bearing on the matter because they only prove that the requirements given in D1 are even more stringent than necessary to achieve an adherent impervious platinum coating which guarantees long term protection of the underlying ceramic substrate from corrosion by the molten glass.

It follows from the above that a skilled person who aims at producing a non-porous platinum coated ceramic article impermeable to reactions with molten glass, has been able to do so when putting into practice the technical teaching given in document D1. It may be true that the appellants' experiments show that the process described in D1 does not in all circumstances and in its broadest aspects successfully lead to a non-porous product. As has been demonstrated by the analysis of the patent in suit by Mr Chandler annexed to the appellant's letter of 20 September 1999, this statement is also true for the patent in suit. Since according to the established jurisprudence, a technical teaching is not insufficiently disclosed if, on encountering occasional lack of success despite strict adherence to prescribed limits for certain variables, there is enough information concerning the effect of those variables to enable a skilled worker to achieve success and if only routine experiments are necessary to convert failure into success. The Board is convinced that the patent in suit still fits this standard and, therefore, meets the requirements of Article 100(b) EPC. Since the specifications given in document D1 are not less detailed, the application of the same standard to its disclosure must necessarily lead to the conclusion that it is equally enabling as the one of the patent in suit.

In view of these considerations, the technical subject matter disclosed in document D1 does not represent a mere "desideratum" and - following the approach taken in decision T 595/90 - therefore is suitable to anticipate the claimed subject matter.

4. Novelty

Claim 1 of the patent in suit defines an external surface of the platinum or platinum alloy coating which is "non-porous". The Board concurs with the position of the opposition division on this point that this term is not unambiguously defined in the patent and, considering the patent as a whole, claim 1 is construed as meaning a surface of a Pt-coating which is able to withstand molten glass and to protect the underlying ceramic substrate from attack by molten glass. This interpretation is supported by the examples of the disputed patent in which the platinum coating was found to be "protective" or "fully protective" to the substrate.

Like the patent in suit, document D1 GB-A-1 242 996 is concerned with a platinum or platinum base alloy coating on a refractory material so as to protect against reactions between the refractory and molten glass or other hot substances in contact with the coating. In particular, the plasma sprayed platinum coatings are specified to be impervious, continuous and adherent to the refractory (cf. D1, page 1, lines 11 to 23). The coatings having a thickness of 4 to 5 mils (102 to 127 µm) are made impervious and impermeable to reactions between the underlying refractory and the molten glass by utilizing a spray velocity of at least 100 feet/second, by selecting a narrowly ranged particle size of Pt-powder (20 to 44 microns) and by heating the coating on the refractory to a temperature of at least 1250 C (cf. page 2, lines 10 to 33; lines 81 to 92). If desired, the surface of the coating can be further smoothened by suitable grinding and polishing (cf. page 2, lines 93 to 99). As set out in the examples 1 and 3 given in document D1, the molten glass on the coated heat treated blocks (static contact, 1250 C) did not contain any blisters or seeds after 7 days (example 1) or 1 day (example 3; 1450 C ). In examples 2 and 4, the heat treated coating was placed in contact with a mass of flowing glass at 1500 C for 7 days (example 2) without observing blisters of seeds in the glass. The examples given in document D1, therefore, attest to the impervious or "non-porous" nature of the platinum coating in that reactions between the molten glass and the ceramic material have not been observed. Consequently, the subject matter of claim 1 is anticipated by the disclosure of document D1.

As to the patentee's arguments relating to the meaning of the terms "impervious or impermeable to reactions" in document D1 and "non-porous" used in the patent in suit, it is noted that the patent specification does not comprise a particular test method in order to verify the general property "non-porous". Thus the criterion whether or not the platinum coating acts as a "reliable barrier" to protect the ceramic substrate from reacting with the molten mass of glass is left as the decisive one. The platinum coatings according to document D1 were found to withstand attack by molten glass for seven days or more and, therefore, this property cannot have been achieved other than by the process disclosed in document D1. Hence, contrary to the patentee's position, the feature "impervious" or "impermeable to reactions" in document D1 must be equated with the feature "non-porous" given in claim 1 of the patent in suit.

Nor can the Board recognize any contradiction between the teaching of document D2 and D1. D2 essentially aims at increasing the adherence or peel strength of the platinum coating on hard dense refractories rather than making the Pt-coating impervious. To this end, an intermediate oxide layer was applied interjacent to the ceramic substrate and the platinum coating. Strong mechanical bonding of the platinum to the intermediate oxide layer is achieved by the platinum forming roots with the pores and crevices of the rough oxide layer and tenaciously adhering thereto. In a specific example given in column 4, lines 13 to 18 of document D2, a very thin platinum coating of 3 mils (76 µm) - thus having a thickness lower than that in D1 (4 to 5 mils corresponding to 102 to 127 µm) - was made impervious by cladding it with a sheet of platinum of suitable thickness. Although the final thickness of the double (= sprayed and clad) Pt-coating is not known from document D2, a "suitable platinum sheet thickness" of about 250 µm would be adequate as alleged by the appellants at the oral proceedings. This is corroborated by document D9 page 49, left hand column to right hand column, second paragraph and page 55, left hand column, lines 16 to 25. Hence, such a double Pt coating would still be within the scope of claim 1 of the disputed patent.

In view of these considerations, the subject matter of claim 1 is not novel and claim 1, therefore, not allowable.

6. Apportionment of costs

According to Article 104(1) EPC a deviation from the rule that each party of the proceedings shall meet its own costs is only possible for reasons of equity. More specifically, a party which behaves or acts in the proceedings in breach of its equitable obligations or in an irresponsible or even malicious manner, may have to bear the costs it caused thereby to other parties.

The appellants' discussion with their expert were, without any doubt, not the consequence of any unfair conduct on the party of the respondents. Rather, they were a means of the appellants' choice within their endeavour to defend their position and to challenge that of their adversary. Thus, there is no ground for awarding the respective or any other costs to the appellants.