T 0516/93 (Elongated sintered article/SUMITOMO) 02-04-1997

Reasons for the Decision

1. The appeal is admissible.

2. The amended claims 1 to 13 are considered to meet the requirements of Article 123(2) EPC. Claim 1 is based on the combination of claims 1 and 3 as originally filed with features disclosed in the original description and in original claim 20. In particular, it is indicated in the latter that the metal pipe is made of silver, and the limitation of the process to the production of an "oxide superconductor wire" is supported by the disclosure at page 1, third paragraph, or page 5, lines 6-7 of the application as filed. The temperature range for the hot-plastic deformation is directly and unambiguously derivable from the disclosure in the original claims 2 and 3 and at page 23 of the description (see "sample No. Ag-20" which was subjected to a hot-plastic deformation at 750°C). Claims 2 to 6 and 9 are based upon the original claims 4 to 8 and 11 respectively. Claims 7 and 8 essentially correspond to original claims 9 and 10 and contain additional information stated at page 8, lines 2-3 and page 7, line 2 of the description. The subject matter of claims 10 and 11 is directly derivable from the original claims 13, 14, 17 and page 11 of the application as filed (second and third paragraphs).

3. D1 discloses a method for manufacturing a superconductive oxide wire, comprising the steps of filling a pipe made of a metal extending in the direction of the longitudinal axis thereof with a powder of a superconductive oxide material, forming the resulting conductive composite body into a wire by wire working and/or rolling in the direction of the longitudinal axis and heat treating the wire so as to sinter the superconductive oxide material (see claim 4). The body may be formed into a wire by drawing and/or rolling (col. 3, lines 4-7). In examples 3 to 6 of D1 a powder of a superconductive oxide material is charged into a silver pipe and the resulting conductive body is subjected to repeated extrusion to gradually reduce its diameter and form a wire. The latter is then cold rolled to obtain a tape-shaped wire which is subsequently sintered at a temperature of 910°C for several hours in an oxygen atmosphere and then gradually cooled to room temperature. In examples 7 and 8, the silver pipe is filled with the superconductive oxide powder and the composite body is subjected to extrusion and then to the sintering step. The process used in these examples does not involve a hot-plastic deformation at a temperature within the range defined in claim 1.

In example 2, a mixture of powders of barium oxide, yttrium oxide and copper oxide is charged into a copper pipe (inner diameter 20 mm). The pipe filled with the mixture is gradually wire-formed while being subjected to heat treatment at a temperature of 950°C in an argon atmosphere, thereby forming the pipe into a wire of 1 mm diameter and obtaining a conductive composite body. The latter is then heat treated at 950°C in an argon atmosphere for five hours. Thus, the process of example 2 comprises a hot-plastic deformation of the copper pipe containing the powder mixture, at a temperature which falls within the range defined in amended claim 1 as well as a subsequent sintering step. The claimed process differs from this process in that the hot-plastic deformation is applied to a silver tube filled with a superconductive oxide powder. It follows from the above that the process of amended claim 1 is novel over D1.

D2 discloses a process for producing a sheathed dispersion strengthened metal rod or tube. The dispersion strengthened metal powder is densified in a metallic sheath or container by size reduction in a plurality of stages, some or all of which may be carried out at elevated temperature, e.g. 1000°F (538°C) or higher, in particular 1450-1650 F (788-899°C), the said stage size reduction being preferably performed until full density is obtained (see page 1, lines 1-4, page 2, lines 25-29, page 4, lines 1-28, page 22, lines 21-26). The dispersion strengthened metal is particularly copper, but metals such as nickel, iron, silver and steel may also be used (see pages 6 and 7). The sheath-forming container is made of a metal which, during the size reduction operation, develops a cold worked tensile strength relatively close to that of the ultimate tensile strength of the dispersion strengthened metal core. The container is formed for example of a ferrous material such as steel, stainless steel, nickel, cobalt, copper or copper/nickel alloys (see page 8, lines 10-25, Examples, and claims 23-29). As pointed out by the appellant, this document neither discloses the use of silver as metal for the sheath-forming tube nor the use of a superconductive oxide material for the filling powder to be introduced into the tube. Therefore, the process of amended claim 1 is new over D2.

Claim 1 also meets the requirement of novelty over the citations of the search report and D5.

4. Taking into account that, on the one hand, only novelty had been examined by the examining division, and, on the other hand, the new citation D5 has been introduced into the procedure at the appeal stage because of its relevance to the claimed subject matter, the board finds it appropriate to remit the present case to the first instance for further prosecution and thus to allow the corresponding appellants' request.

5. Pursuant to Rule 67 EPC, reimbursement of the appeal fee is ordered where the appeal is deemed to be allowable, if such reimbursement is equitable by reason of a substantial procedural violation. It follows from the above that the appeal is allowable. In support of their request for refund of the appeal fee the appellants merely argued that they were not given the opportunity to present amended claims after their response to the first communication.

Neither Article 113(1) nor Article 96(2) EPC requires that the applicants be given a repeated opportunity to comment on the examining division's submissions so long as the decisive objections against the grant of a patent remain the same. The expression "as often as necessary" in Article 96(2) indicates that the examining division has a discretion in each individual case as to whether or not to invite further observations from an applicant before issuing a decision. In particular, this discretion should be exercised in favour of inviting further observations if there is a reasonable prospect that such an invitation could lead to the grant of the patent application. Refusing a patent application after a single communication would constitute a substantial procedural violation in particular if the decision of refusal contravened the provisions of Article 113(1) EPC (ie if the general procedural principle of "a right to be heard" were not respected) or if the examining division had exercised its discretion in an unreasonable way or taking into account the wrong principles (see in particular T 162/82, OJ EPO, 1987, 533; T 640/91, OJ EPO, 1994, 918; and T 951/92, OJ EPO, 1996, 53).

In the present case, the first communication indicates inter alia that the subject matter of claims 1 to 20 as filed is not new over D1 since it is fully anticipated by example 2 of D1 and that claims 1 to 12 also appear to lack novelty over example 1 of D2. In reply thereto, the appellants filed amended claims with an amended claim 1 corresponding to a combination of the original claims 1 and 2, which were both said to lack novelty in the first communication. They submitted in substance that amended claim 1 appeared to be new since neither D1 nor D2 taught a process according to the preamble of claim 1 and comprising the features recited in the characterising part thereof. The appellants gave no further explanation as to why they considered that the two cited examples did not disclose the said features.

A comparison of the first communication with the subsequent decision of refusal shows that there is no essential difference between the reasonings put forward therein as regards lack of novelty. The decision contains some additional explanations about the temperature of the hot plastic deformation in example 2 of D1 and in example 1 of D2; however the first communication already clearly set out the essential legal and factual reasoning leading to the finding in the subsequent decision that the subject matter of amended claim 1 (ie original claims 1 and 2) lacked novelty over the teaching of D1, example 2, or D2, example 1. This was not contested by the appellants in their reply to the communication of the board. The general procedural principle of "a right to be heard" was thus not violated. Furthermore, the board cannot derive from the particular circumstances of this case, in particular from the content of the first communication, the appellants' reply and the appealed decision, that the examining division has exercised its discretion on the basis of wrong principles or in an unreasonable way.

For the preceding reasons the board has come to the conclusion that no substantial procedural violation took place. Therefore, the request for refund of the appeal fee must be refused.

6. In view of the outcome of the present decision, it was not necessary to hold oral proceedings, since the latter were requested only if the amended set of claims were to be refused.