T 2555/18 20-10-2022

Reasons for the Decision

1. Admissibility of the appeal

1.1 The respondent requested that the appeal not be admitted. The arguments concerning sufficiency of disclosure amounted to a mere repetition of those before the opposition division, clarity could not be examined following G 3/14 and the analysis of obviousness was not complete. For these reasons, the statement of grounds of appeal did not indicate the reasons why the appealed decision should be set aside meaning that it did not fulfil the requirements of Rule 99(2) EPC.

1.2 The appeal is admissible for the following reasons.

The opposition division concluded that it was credible that the implants of the claimed invention migrated less than those of the closest prior art D2. As the prior art did not hint at the claimed solution to the problem of providing an improvement, that solution was inventive.

In the grounds of appeal the appellant set out its arguments as to why such an improvement over D2 had not been achieved. The problem underlying the claimed invention should thus be seen as the mere provision of an alternative, which was not inventive.

In the board's view, this line of argument is sufficient for the appeal to comply with Rule 99(2) EPC. The appellant provided arguments as to why the opposition division's conclusion concerning inventive step was not correct. In these circumstances, the matters of whether other issues of the appealed decision were sufficiently reasoned in the grounds of appeal and whether the appellant's line of argument is convincing have no bearing on the admissibility of the appeal.

2. Admissibility of D23 and D24.

2.1 The board decided not to admit D23 and D24 into the proceedings.

2.2 Experimental evidence D23 and document D24 were filed with a letter dated 15 December 2020, after the board's communication under Rule 15(1) RPBA 2020.

The filing of D23 and D24 represent an amendment of the appellant's case. Their admissibility into the proceedings is thus enshrined by Article 13(1) RPBA 2020.

2.3 Article 13(1) RPBA 2020 requires the appellant to provide reasons for submitting D23 and D24 at that stage of the appeal proceedings. No reason was provided, however, prior to the oral proceedings before the board.

2.4 As far as the relevance of these documents is concerned, the appellant argued that experimental evidence D23 compared particles of the the size required by claim 1 with smaller particles and showed that no effect in terms of cohesion and hence on implant migration arose from that size difference. D24 was to provide background for the experimental evidence provided.

The particles of the closest prior art D2 (0.561 mm) are, however, an order of magnitude larger than those used in D23 as comparison (0.050 mm). Therefore, the evidence provided does not reflect the particles of D2 and is thus not suitable for showing a lack of technical effect. For this reason, D23 and D24 are not prima facie relevant.

2.5 The appellant argued that Article 12 RPBA 2007 only required a party's case to be as complete as possible, but not necessarily complete, in the statement of grounds of appeal.

Article 12(2) RPBA 2007 stipulates, however, that the statement of grounds of appeal and the reply are to contain a party's complete case. The appellant's argument is not convincing.

2.6 For these reasons the board decided to exercise its discretionary power not to admit D23 and D24 into the proceedings (Article 13(1) RPBA 2020).

3. Sufficiency of disclosure

3.1 The opposition division concluded that the alleged dependence of the particle size on the method of measurement could, at the most, affect the clarity of the claimed subject-matter but not the sufficiency of disclosure of the claimed invention.

3.2 The board informed the parties in a communication that it was leaning towards agreeing with the opposition division's conclusion.

3.3 The appellant brought no subsequent argument on this issue either in writing or at the oral proceedings before the board.

There is thus no reason to depart from the board's preliminary view that the claimed invention is sufficiently disclosed for it to be carried out by a skilled person.

4. Clarity

The appellant argued that the feature "major volume" in claim 7 was not clear. It is, however, a feature of the granted claims and is thus excluded from examination of its clarity in the present opposition appeal proceedings following G 3/14. This was undisputed at the oral proceedings before the board.

5. Inventive step

5.1 Claim 1 is directed to particles which are injectable and suitable for implantation and have a size of from 1.5 to 5 mm in saline. Claim 7 relates to a soft-tissue augmentation implant comprising particles, wherein a major volume of said particles have a size of from 1.5 to 5 mm when subjected to saline.

5.2 Closest prior art

The opposition division and the parties considered that document D2 was the closest prior art.

It was not disputed that document D2 discloses particles and implants which differ from those of the subject-matter of claims 1 and 7 only by virtue of the particle size.

The particles disclosed in D2, subjected to demineralised water, have a size of 0.561 mm, 0.390 mm and 0.220 mm (paragraph 2.1) and are thus smaller than required by claims 1 and 7. The latter should have a size in the range of from 1.5 to 5 mm.

5.3 Technical problem underlying the invention

5.3.1 The respondent defined the technical problem underlying the claimed invention as being to provide implants with reduced migration after implantation in soft tissue.

The respondent relied on the examples of the opposed patent and the experimental evidence filed as D12 during opposition proceedings to show that this problem had been credibly solved.

The appellant argued that the problem as formulated by the respondent had not been credibly solved. In the examples of the patent, the particles were deeply implanted. Any effect on migration was only the result of the implantation technique. In addition, the evidence filed as D12 could not show an effect across the whole scope of the claimed subject-matter.

5.3.2 The question of whether the problem as formulated by the respondent has been solved in all aspects can, however, be left aside. The reason is that, even if the technical problem is formulated merely as the provision of alternative particles and implant suitable, like those of D2, for soft-tissue augmentation, the proposed solution is not obvious for the reasons that follow.

5.4 Solution

The solution to this technical problem is provided by the claimed particles and implant, characterised by a particle size in the range of from 1.5 to 5 mm when subjected to a physiological salt solution.

5.5 Success

5.5.1 At the oral proceedings before the board, the appellant argued that even this less ambitious problem had not been credibly solved.

The appellant argued that experimental evidence D12 merely contained two points, which could not represent every embodiment of claims 1 and 7. In addition, the evidence in the patent only related to the implantation of particles with homogeneous size distribution. This was, however, not a feature of claim 7, which only required a "major volume" of such particles to be present.

5.5.2 However, according to example 2 of the patent, satisfactory chin augmentation could be obtained for at least three months. Example 4 relates to breast-tissue augmentation and discloses that, twelve months following implantation, the breasts were still in good shape with thin nodular implants. This is the same time span as for Restylane implants of the closest prior art D2, as disclosed on page 286, left column, lines 22-23, of D3. The data in the patent thus shows that the claimed particles and implants are, like those of D2, suitable for implantation.

The board thus concludes that the problem of providing alternative particles and implants that are suitable, like those of D2, for soft-tissue augmentation has been credibly solved.

5.6 It thus remains to be decided whether the proposed solution to the objective problem defined above would have been obvious for the skilled person in view of the prior art.

5.6.1 The appellant argued at the oral proceedings before the board that D3 taught the claimed solution.

Like D2, D3 relates to soft-tissue fillers for wrinkles, folds and volume augmentation. The first full paragraph on page 286 of D3 mentions products of the patent proprietor.

Restylane has 100 000 particles per millilitre. According to paragraph [0004] of the patent this product has a particle size of 0.4 mm.

Perlane has, according to D3, 8000 particles per millilitre. Paragraph [0004] of the patent refers to this product as having about 10 000 particles per millilitre and a mean particle size of approximately 0.8 mm.

Lastly, D3 mentions that the thickest product, Perlane Plus, will have 4000 particles per millilitre. Its particle size is not disclosed.

According to the appellant, in the absence of an effect in terms of migration, particles larger than those of D2 would have been obvious for the skilled person.

However, the largest particles in D3 are nevertheless smaller than those of claim 1. D3 thus teaches that the particle size of the closest-prior-art particles, Restylane, could be increased to some extent, but not as much as required by claims 1 and 7.

A skilled person, seeking alternative particles for a soft-tissue implant, would have had no reason to conclude that particles having thrice or more the size of those of D2 could form a suitable implant and be injected despite their size.

5.6.2 The appellant argued that the claimed particles would have been obvious from D2 alone. However, D2 merely relates to the commercial product Restylane, with smaller particles. It does not hint at larger particles.

5.6.3 In its written submissions, the appellant argued that, as a mere alternative, documents D1, D11, D13 and D21 taught the claimed solution.

5.6.4 Documents D13 and D21 were only relied upon at the oral proceedings before the opposition division. Neither the minutes nor the decision explicitly refer to any particular passage of these documents. The appealed decision only mentions that D13 and D21 did not relate to implant migration.

In the absence of specific details, the board cannot see the relevance of these arguments.

5.6.5 With respect to D1 and D11, the appellant referred to its notice of opposition dated 2 May 2017.

Both D1 and D11 relate to particles for implants, which can have the size required by claims 1 and 7.

D1 discloses implants made of acrylonitrile, which is chemically very different from cross-linked hyaluronic acid.

D11 discloses a long list of materials, among which gelatin is preferred. Glycosaminoglycan, mentioned in column 5, line 44, includes not only hyaluronic acid but also other substances. Cross-linking is only disclosed as an option in column 5, lines 53 and following.

The skilled person looking for an alternative to the particles of D2 would not have considered the particle sizes disclosed in D1 or D11 to be of general application to every implant material, let alone to cross-linked hyaluronic acid. Documents D1 and D11 thus do not hint at the claimed solution.

5.7 The board thus concludes that the particles of claim 1 and the implant of claim 7 are inventive, as required by Article 56 EPC.

6. The appellant has not put forward further arguments against the subject-matter of independent claims 6, 10 and 11, or any of the dependent claims on file other than those already rejected in the context of claims 1 and 7.