T 0596/01 10-04-2003

Reasons for the Decision

Main Request

1. Article 100(c) EPC

Compared to the application as filed, claim 1 of the patent as granted contains the feature "directing a laser beam...to selectively sinter...in a first cross-sectional region of the part" whereas in claim 1 of the application as filed the corresponding feature was "heating...a cross-sectional region of the part". In the application as filed on page 4, line 14 reference is made to "sintering or melting temperatures". On page 4, lines 27 to 28 reference is made to "the temperature to which the directed beam subjects the powder". On page 6, lines 26 to 29 reference is made to "The control mechanism operates the laser to selectively sinter...layers sintered together". On page 9, line 31 to page 10, line 11 it is explained that thermal energy may enable chemical reaction. The reaction may occur during the application of directed energy. Alternatively, the directed energy may melt or sinter the materials and a subsequent heat treatment cause the reaction. According to page 17, lines 34 to 35 the sintering may be effected on a polymer to cause the polymer to flow. According to claim 8 as filed the heating step comprises directing an energy beam and according to claim 9 the directing step of claim 8 comprises directing a laser.

From the above mentioned parts of the application as filed the Board concludes that the step set out in claim 1 regarding directing a laser to produce sintering is disclosed in the application as filed. Claim 1 as filed however contained a reference to heating in this respect. According to the normal technical understanding of sintering this process implies causing a material to coalesce under the influence of heat. Each of the above-mentioned references to sintering in the application as filed is consistent with this definition.

The respondent has argued sintering implies densification and that cross-linking a polymer causes densification. Further, a polymer may be cross-linked by a laser without the production of heat so that sintering may be affected without heating. The Board considers that this line of argumentation is not consistent with the normal technical meaning of the term sintering which requires some heating. Moreover, the description of the patent is consistent with the normal technical meaning. Therefore, the Board considers that claim 1 as granted does not offend Article 123(2) EPC in this respect.

2. Novelty

In the opinion of the Board the subject-matter of claim 1 is novel because neither of documents D1 or D2 disclose the characterising feature of the claim. The Opposition Division in their decision considered that an alloy was a chemical compound. The Board cannot agree with the Opposition Division on this point. It is well established that an alloy may comprise a mixture, a solid solution or an intermetallic compound. In the opinion of the Board only an intermetallic compound may be considered a chemical compound in the sense of claim 1 since mixtures and solutions in principle form a physical association but not a chemical association. The description of the patent is consistent with this view as it describes intermetallic compounds as chemical compounds, but does not indicate mixtures or solid solutions as chemical compounds.

In document D1 there is a disclosure of forming bronze together with the other features of claim 1. Bronze is well-known to have phases which are intermetallic compounds, but also forms solid solutions depending upon the composition and the heat treatment. The only indication in the document of the form of bronze is an indication that the tin is dissolved into the copper in the solid state. Thus, in document D1 there is no indication that an intermetallic phase of bronze is formed, so that there is no disclosure of the characterising feature of claim 1.

In document D2 the features of the preamble of claim 1 are disclosed and the appellant has not disputed this view. The document further mentions the presence of first and second materials in that there is a reference to the powder materials being used may be "composite". This means that the powder comprises more than one material. The document at several instances also makes reference to a "chemical change", to a difference in "chemical property", and to "chemical bonding". The Board is thus satisfied that the document discloses a chemical reaction in the layer of powder material. However, the Board is not satisfied that this chemical reaction necessarily results from a chemical reaction between two materials. Chemical reactions may also occur when heating a single substance. Even in the case of heating a composite powder chemical change can result from a chemical change in one constituent alone without any interaction between the constituents. There is thus no unambiguous disclosure in document D2 of a chemical reaction between two constituents.

Therefore, the subject-matter of claim 1 is novel in the sense of Article 54 EPC.

Inventive step

3.1. Closest prior art

The closest prior art is represented by document D1 which discloses a method comprising the features of the preamble of claim 1.

3.2. Problem to be solved

The appellant considered that the problem to be solved is to form a compound which cannot be sintered. The Board cannot agree with this problem since the characterising feature of claim 1 does not necessarily solve this problem. The characterising feature of claim 1 merely requires the formation of a chemical compound. The chemical compound may be any chemical compound. There is no feature in the claim which ensures that the compound formed cannot be sintered. Therefore, the claim does not contain the features necessary to ensure that this problem is solved.

The appellant argued that it is sufficient that the features of the claim can solve the problem and it is irrelevant that the problem is not solved throughout the whole breadth of the claim. The Board cannot agree with this view. If an inventive step is to be based on the solution to a particular problem then it is essential that the problem is solved throughout the breadth of the claim. Otherwise, a patentee would obtain protection for subject-matter which does not solve the problem and does not involve an inventive step.

According to column 3, lines 10 to 12 of the patent the problem to be solved is to produce a part by applying energy to a powder wherein the material of the part has properties which differ from those of the material in the powder. This problem however is already solved in document D1 since bronze, which is produced from tin and copper, has properties which differ from those of each of tin and copper. The Board therefore concludes that the objective problem to be solved by the features of claim 1 is to provide an alternative solution to the problem stated in the patent.

3.3. Solution to the problem

The solution to the problem is that the first and second powder materials are reacted to form a chemical compound of said materials.

3.4. The solution to the problem is obvious for the following reasons:

It is well established that heating can change physical and/or chemical properties. This is mentioned in document D2 where on page 11, lines 8 to 9 explicit reference is made to a laser beam changing the physical or chemical properties of a powder. Thus, the skilled person is aware that properties can be changed either physically or chemically. The skilled person is also aware that when alloys, such as bronze, are formed then either solutions, i.e. physical change, or compounds, i.e. chemical change, can be formed depending upon the percentages of the constituents and/or the treatment process. Thus, the skilled person knows that when bronze or another alloy is being formed he has a choice of effecting change either physically or chemically to arrive at a material which has differing properties to the starting material. Alloys are indeed formed for the purpose of producing materials which have useful properties which are not obtained in the pure constituent materials. Document D1 discloses such production, i.e. producing bronze, at least physically since dissolving is mentioned. Since the alternative method of achieving the goal, i.e. via a chemical reaction, is well-known and specifically mentioned in document D2 there is no inventive step involved in choosing this alternative method.

The appellant has argued that the skilled person reading document D1 would want to make Alpha-bronze which is useful and this would be lead him away from forming a chemical compound. The Board cannot agree with this view. Although document D1 mentions dissolving there is no indication that this should be to form Alpha-bronze. There are other forms of bronze which are well-known which have useful properties. These other forms include intermetallic compounds. The skilled person would consider solving the problem by providing the alternative solution of forming bronze in a phase involving an intermetallic compound. Intermetallic compounds are within the scope of claim 1 and indeed the main embodiments of the patent are intermetallic compounds. In any case claim 1 of the patent has no features which ensure any particular properties of the chemical compound being produced. Therefore arguments based on the usefulness of chemical compounds or on prejudices against forming chemical compounds are baseless given the wording of the claim. The characterising feature of claim 1 is therefore obvious to the skilled person.

3.5. Therefore, the subject-matter of claim 1 of the main request does not involve an inventive step in the sense of Article 56 EPC.

First Auxiliary Request

4. Article 123(2)

In the application as filed there is a disclosure on page 21, lines 5 to 9 of a compound formed from the stoichiometrical quantities of the constituents. It is then stated that an excess amount of one of the constituents may be supplied, i.e. non-stoichiometrical quantities. The extra feature of claim 1 corresponds to these two disclosed possibilities. There is therefore no addition of subject-matter.

5. Inventive step

The extra feature of claim 1 of this request indicates relative proportions of the powder materials which form the chemical compound. It does not require the stoichiometrically exact proportions for the compound, but merely that the proportions permit the formation of the compound. Indeed, in the description it is explicitly allowed that one of the constituents may be in a quantity greater than the stoichiometrically correct quantity, so that after formation of the compound some of the one constituent will remain in excess. In the opinion of the Board this feature was already inherently included in claim 1 of the main request. Since claim 1 of the main request requires the formation of a chemical compound from two powder materials it is clear that there must be provided some of each material. Claim 1 of the first auxiliary request specifies no more than this. The appellant argued that the selection step avoided any chance anticipation. However, the question with respect to inventive step is not that of a chance anticipation but of an obvious measure. This argument does not therefore support an inventive step.

Therefore, the subject-matter of claim 1 of the first auxiliary request does not involve an inventive step in the sense of Article 56 EPC.

Second Auxiliary Request

6. Non-admittance of the request

During the oral proceedings before the Board the appellant withdrew his then existing second auxiliary request which had been filed with his appeal grounds. In its place he submitted a new second auxiliary request which added the features of the dependent claims 2 to 4 as granted to claim 1 of the first auxiliary request. The Board therefore has to decide whether to admit this request at this stage of the proceedings.

With the invitation to the oral proceedings the Board provided the parties with its provisional opinion. In that opinion the Board provisionally considered that none of the requests on file of the appellant was likely to succeed. The appellant was thus aware well before the oral proceedings that further requests might be helpful to him. The appellant however did not file any further requests.

The Board cannot therefore identify any extenuating circumstances which might justify exceptionally admitting the late filed request. The appellant has argued that he did not know if the Board saw the problem with his other requests in the definition of the terms of the claims or in a more general problem. The Board cannot agree with this line of argumentation. In its provisional opinion the Board not only indicated its negative view of the requests but gave clear reasons to justify the view. The argument of the representative that he did not know the problem with the requests is therefore not justified.

The respondent has pointed out that the new request differs substantially from the existing requests and reasonably requested further oral proceedings in the case that the request is admitted into the proceedings. It is indeed clear that the new request would require the respondent to develop new lines of argumentation and to review the disclosures of all the documents in the proceedings. In order that the respondent could reasonably respond to the new request a further oral proceedings would be necessary.

In these circumstances the Board exercises its discretion not to admit the second auxiliary request of the appellant (see "Guidance for parties to appeal proceedings and their representatives", OJ 1996, 342 point 3.3).